Model:BT6001 |
Color: White |
|
PHYSICAL PROPERTIES- Liquide Material |
Appearance |
White |
Density |
1.13g/cm³@25℃ |
Viscosity |
355 CPS@28℃ |
Dp |
0.145 mm |
Ec |
9.3 mJ/cm² |
Mechanical Preperties of Post-Cured Material(90-minute UV post-cure) |
Hardness, Shore D |
84 |
Flexural modules, Mpa |
2,673-2,781 |
Flexural strength, Mpa |
68-75 |
Tensile modulus, Mpa |
2,167-2,402 |
Tensile strength,Mpa |
26-32 |
Elongation at break |
12-21% |
Impact strength, noticed lzod, J/m |
57-71 |
Heat deflection temperature,℃ |
52 |
Glass transition, Tg ℃ |
63 |
Coefficient of thermal expension,/℃ |
97*E-6 |
Density, g/cm3 |
1.16 |
|
|
Model:BT6005 |
Color: Light yellow |
|
PHYSICAL PROPERTIES - Liquid Material |
Appearance |
Light yellow |
Density |
1.11-1.15 g/cm³@25℃ |
Viscosity |
450-530 CPS@27℃ |
Dp |
0.14-0.16 mm |
Ec |
7.1 ~ 8.1 mJ/cm² |
Mechanical Properties of Post-Cured Material(90-minute UV post-cure) |
Hardness, Shore D |
76~91 |
Flexural modulus, Mpa |
2,683-2,781 |
Flexural strength, Mpa |
72-77 |
Tensile modulus, Mpa |
2,641-2,783 |
Tensile strength, Mpa |
43-57 |
Elongation at break |
7-13% |
Poisson's Ratio |
0.41-0.46 |
Impact strength notched Izod, J/m |
27 - 41 |
Heat deflection temperature, ℃ |
72~86 |
Glass transition, Tg, ℃ |
79 - 96 |
Coefficient of thermal expension, /℃ |
84 ~ 98 *E-6 |
Density, g/cm3 |
1.12 ~ 1.18 |
Dielectric Constant 60 Hz |
4.2 ~ 5.1 |
Dielectric Constant 1 KHz |
3.4 ~ 4.2 |
Dielectric Constant 1 MHz |
3.1 ~4.2 |
Dielectric Strength kV/mm |
12.5 ~ 16.8 |
Model:BT6008 |
Color: Clear |
|
PHYSICAL PROPERTIES - Liquid Material |
Appearance |
Clear |
Density |
1.12 g/cm³@25℃ |
Viscosity |
312 ~ 420 CPS@25℃ |
Dp |
0.18 mm |
Ec |
7.7 v, -mJ/cm² |
MECHANICAL PROPERTIES OF POST-CURED MATERIAL(90-MINUTE UV POST-CURED ) |
Hardness, Shore D |
83 |
Flexural modulus, Mpa |
2,670-2,870 |
Flexural strength,Mpa |
75-84 |
Tensile modulus, Mpa |
2,590-2,760 |
Tensile strength, Mpa |
44-62 |
Elongation at break |
7-11% |
Impact strength, noticed Izod, J/m |
27-38 |
Heat deflection temperature, ℃ |
40 ~ 51 |
Glass transition, Tg, ℃ |
42 ~ 58 |